Calcium Aluminate Cement CA-70 GB201-2000 CA-70 Setting time Initial(min) >=30 >=30 Final(min) <=360 <=360 Flexure (Mpa) 1d 5.0 5.5 3d 6.0 6.5 Compressive (Mpa) 1d 30 5
Aluminate Cement Chemical Composition Index of inspection CA-50 GB201-2000 A500 A600 A700 A900 Al2O3 % >=50,<60 >=50,<60 >=52,<60 SiO2 >=8.0 >
Fused Mullite Fused mullite, using high purity quartzite and industrial alimina powder as main starting materials, smelting in tilting electronic are furnace, is a
a-type alumina 1 a-alumina powder is used snow-capped mountains brand a-alumina as raw material grinding made a dry grinding process and wet. 2 For unshaped refract
white fused alumina APPLICATION FIELD 1.AS REFRACTORIES White fused alumina is the main starting matriel to producehigh-grade unshaped and shaped refractories and is wid
Calcium aluminate Flux FX-50 1 Calcium aluminate Flux FX-50 is used in ladle metallurgy as a slag control agent. With Flux FX-50, plant productivity can be increased and costs
White Corundum White corundum AL2O3 content higher than 98% higher than the hardness toughness than Brown Fused Alumina Brown Fused Alumina, there is a good cutting
High Aluminate Bauxite 1 It is widely used in metallurgical industry, building material refractory materials. 2 It has different size :0-1mm, 1-3mm, 3-5mm, 5-8m
ferractory brick We have differemt model number bricks can meets yous different needs Model number: T3(standard brick) T14, T19, T20, T29, T38, T39 and others This
a-type calcined alumina 1.The a-type calcined alumina produced by our company is an alumina product calcined with rotary kiln with quality raw materials at resonable calcina
a-type calcined alumina 1.The a-type calcined alumina produced by our company is an alumina product calcined with rotary kiln with quality raw materials at resonable calcina
a-type calcined alumina 1.The a-type calcined alumina produced by our company is an alumina product calcined with rotary kiln with quality raw materials at resonable calcina
Calcium Aluminate Cement CA-70 1 the cement of Al2O3 is controlled in 68-72%. 2 the eariy strength is high and strength in medial temperture is also high, the refractorinessis mor
Aluminate Cement Chemical Composition Index of inspection CA-50 GB201-2000 A500 A600 A700 A900 Al2O3 % >=50,<60 >=50,<60 >=52,<60 SiO2 >=8.0 >
Aluminate Cement Chemical Composition Type of product GB201-2000 CA70 CA-70 CA-75 GB201-2000 CA-80 CA-80 Al2O3 % >=68,<77 >=68,<72 >=73,<77 >=77